A STUDY ON PREPARATION AND HYDRIDING OF -Mg2Al3 AND -Mg17Al12

Sari

ABSTRACT

A Study on Preparation and Hydriding OF b-Mg₂Al₃ AND g-Mg₁₇Al₁₂. The mechanism of the synthetic formation of b-Mg₂Al₃ and g-Mg₁₇Al₁₂ has been studied. Mechanical alloying of Mg and Al powders with the atomic ratio of Mg:Al = 2:3 in toluene solution yields b-Mg₂Al₃ compound after milling for 30 h. The g-Mg₁₇Al₁₂ can be formed by heating the b-Mg₂Al₃ at 430 °C under high vacuum. The measured hydrogen capacities of b-Mg₂Al₃ and g-Mg₁₇Al₁₂ as hydrided at 300 °C are 3.2 and 4.9 wt%, respectively. Microstructure of the Mg-Al specimen shows that on hydriding at 300 °C the polygonal shape of the g-Mg₁₇Al₁₂ changes into irregular shapes which are composed of g-MgH₂ and Al.

FREE TERMS: mechanical Alloying, Mg-Al compounds, hydriding

ABSTRAK

STUDI PENYIAPAN DAN HIDRIDING b-Mg₂Al₃ DAN g-Mg₁₇Al_12. Mekanisme pembuatan b-Mg₂Al₃ dan g-Mg₁₇Al₁₂ telah dipelajari. Pemaduan mekanik serbuk Mg dan Al dengan perbandingan atomik Mg:Al = 2:3 dalam larutan toluena menghasilkan senyawa b-Mg₂Al₃ setelah penggerusan selama 30 jam. g-Mg₁₇Al₁₂ dapat terbentuk dengan pemanasan b-Mg₂Al₃ pada suhu 430 °C dalam vakum tinggi. Kapasitas hidrogen terukur dari b-Mg₂Al₃ dan g-Mg₁₇Al₁₂ terhidrisasi pada suhu 300 °C adalah berturut-turut 3,2 dan 4,9% berat. Mikrostruktur dari spesimen Mg-Al menunjukkan bahwa sewaktu hidriding pada suhu 300 °C bentuk poligonal dari g-Mg₁₇Al₁₂ berubah menjadi tak beraturan yang terdiri dari g-MgH₂ dan Al.

KATA KUNCI: pemaduan mekanik, senyawa Mg-Al, hidriding