CHARACTERISTIC OF (AgI)0.44 (LiI)0.22 (AgPO3)0.34 IONIC CONDUCTOR PREPARED BY MELT QUENCHING METHOD

Makhsun Makhsun(1), T. Sakuma(2), E. Kartini(3),


(1) Institute of Applied Beam Science, Ibaraki University Mito 310-8512, Ibaraki, Japan Center for Technology of Radiation Safety and Metrology, Indonesian National Nuclear Energy Agency Jakarta Selatan 12070, Indonesia
(2) Institute of Applied Beam Science, Ibaraki University Mito 310-8512, Ibaraki, Japan
(3) Center for Technology of Nuclear Industry Materials, Indonesian National Nuclear Energy Agency Kawasan Puspiptek, Serpong 15314, Tangerang Selatan, Indonesia
Corresponding Author

Abstract


CHARACTERISTIC OF (AgI)0.44 (LiI)0.22 (AgPO3)0.34 IONIC CONDUCTOR PREPARED BY MELT QUENCHING METHOD. Characterization of (AgI)0.44 (LiI)0.22 (AgPO3)0.34 ionic conductor prepared by melt quenching method have been carried out by using X-RayDiffractometer (XRD), Differential Scanning Calorimeter (DSC) and Inductance (L) Capacitance (C) Resistance (R) meter. X-ray diffraction pattern shows that the compound has a mixture of amorphous and small amount of crystalline formwith several Bragg peaks correspond toAgI. The DSC thermograph shows that an endothermic peak at temperature ~420 K matches with the phase transition ofAgI which reinforces that a number ofAgI are not dissolved in the material of (AgI)0.44 (LiI)0.22 (AgPO3)0.34 . The obtained dc ionic conductivity is around ~10-2 S/cmat ambient temperature. The activation energy has two values, 0.20 eV below ~380 K and 0.15 eV above ~380 K.

Keywords


Solid electrolyte, Super-ionic glass,AgPO3,AgI-LiI-AgPO3