PENGARUH PENGEROLAN PANAS TERHADAP KARAKTER PADUAN Zr-0,6Nb-0,5Fe-0,5Cr. Paduan Zr-0,6Nb-0,5Fe-0,5Cr hasil pengerolan panas telah diteliti karakternya. Tujuan penelitian ini adalah mendapatkan data pengaruh pengerolan panas terhadap karakteristik mikrostruktur, kekerasan dan fasa yang terbentuk dalam paduan Zr-0,6Nb-0,5Fe-0,5Cr. Proses pengerolan panas  paduan Zr-0,6Nb-0,5Fe-0,5Cr dilakukan pada temperatur  800 oC dengan waktu penahanan (soaking time) 1,5 dan 2 jam dan reduksi ketebalan 5–25 %. Hasil penelitian menunjukkan bahwa paduan Zr-0,6Nb-0,5Fe-0,5Cr memiliki struktur Widmanstätten dengan evolusi mikrostruktur menjadi kolumnar terdeformasi dan batang pipih terdeformasi seiring dengan  semakin  besarnya reduksi ketebalan. Selain itu, semakin lama waktu penahanan pada temperatur  800 oC maka ukuran butir relatif lebih besar dan terjadi pembentukan fasa a-Zr dan Zr3Fe. Kekerasan paduan Zr-0,6Nb-0,5Fe-0,5Cr mempunyai kecenderungan yang sama yaitu semakin besar reduksi ketebalan maka semakin tinggi kekerasannya. Paduan Zr-0,6Nb-0,5Fe-0,5Cr  mampu menerima deformasi besar berupa pengerolan panas dengan reduksi ketebalan  25 % dan terbentuknya fasa a-Zr dan Zr3Fe dapat meningkatkan kekerasan dan kekuatan paduan Zr-0,6Nb-0,5Fe-0,5Cr.

Kata kunci: Paduan, pengerolan panas, reduksi ketebalan, mikrostruktur, kekerasan, fasa.


 

ABSTRACT

HOT ROLLING EFFECT ON THE CHARACTERS OF Zr-0.6Nb-0.5Fe-0.5Cr ALLOY. Characters of Zr-0.6Nb-0.5Fe-0.5Cr alloy after hot rolling have been studied. The objective of this research was to obtain of hot rolling effect on the characteristics of microstructures, hardness and phases formed in Zr-0.6Nb-0.5Fe-0.5Cr  alloy. The hot rolling process of alloy carried out at temperature of  800 oC with retention time of 1.5 and 2 hours and a thickness reduction between 5 to 25 %. The results of this experiment showed that the Zr-0.6Nb-0.5Fe-0.5Cr alloy has Widmanstatten structure with microstructure evolving into deformed columnar grains and deformed elongated grains with increasing thickness reduction. Besides, the longer the retention time at temperature of 800 oC is the larger are the grain structures and formation of a-Zr and Zr3Fe phase. The hardness of  Zr-0.6Nb-0.5Fe-0.5Cr alloy has same trends i.e the larger thickness reduction gives higher hardness. The Zr-0.6Nb-0.5Fe-0.5Cr alloy can under go hot rolling deformation at a thickness reduction of  25 %  and the formation of a-Zr and Zr3Fe can increased of hardness and strength of Zr-0.6 Nb-0.5 Fe-0.5 Cr alloy.

Keywords: Alloy, hot rolling, thickness reduction, microstructure, hardness, phase.