KARAKTERISASI KOMPOSISI KIMIA, LUAS PERMUKAAN PORI DAN SIFAT TERMAL DARI ZEOLIT BAYAH, TASIKMALAYA, DAN LAMPUNG

Sari

ABSTRAK

KARAKTERISASI KOMPOSISI KIMIA, LUAS PERMUKAAN PORI, DAN SIFAT TERMAL DARI ZEOLIT BAYAH, TASIKMALAYA, DAN LAMPUNG. Telah dilakukan karakterisasi komposisi kimia, luas permukaan, jari-jari pori, daya serap (adsorption) dan sifat termal zeolit Bayah, Tasikmalaya, dan Lampung. Tujuan karakterisasi adalah untuk memahami karakter ketiga zeolit karena diduga perbedaan jenis zeolit akan menghasilkan karakter komposisi kimia, luas permukaan, jari-jari pori, dan daya serap yang berbeda. Hasil analisis menunjukkan bahwa zeolit Bayah, Tasikmalaya, dan Lampung mengandung unsur kimia Al, Si, P, K, Ca, Ti, Fe, dan S. Dari analisis luas permukaan diperoleh bahwa zeolit Lampung mempunyai luas permukaan 10,0477 m², jari-jari pori 16,0653Å, dan adsorpsi 24,500 ml/g lebih besar dibanding zeolit Tasikmalaya sebesar 6,3319 m², jari-jari pori 16,2350 Å, dan adsorpsi 13,2500 ml/g, dan zeolit Bayah sebesar 8,3528 m², 16,2350 Å, dan 13,250 ml/g. Dari karakterisasi sifat termal diketahui bahwa ketiga zeolit tersebut mengalami pengurangan berat sebesar 5,93% hingga 8,33% yang menyebabkan terjadinya perubahan fase baru yang ditunjukkan oleh reaksi endotermik pada temperatur 150 °C hingga 600 °C dan 850 °C hingga 1000 °C. Ketiga zeolit tersebut mengalami penurunan kapasitas panas hingga temperatur 199,96 °C tetapi di atas temperatur 216,66 °C mengalami kenaikan kapasitas panas hingga temperatur 437,78 °C. Hasil karakterisasi yang diperoleh menunjukkan bahwa perbedaan jenis zeolit tidak memberikan komposisi kimia dan karakter termal yang signifikan yang dibuktikan dengan analisis uji F, namun jelas terlihat perbedaan luas permukaan, jari-jari pori, dan besar adsorpsi dari ketiga zeolit tersebut. Hasil karakterisasi ini diharapkan sebagai langkah awal untuk mengetahui karakter ketiga zeolit untuk digunakan sebagai penukar ion cesium yang akan dilakukan pada penelitian selanjutnya.

KATA KUNCI: zeolit, kompisisi kimia, luas permukaan, jari-jari pori, sifat termal

ABSTRACT

CHARACTERIZATION OF CHEMICAL COMPOSITION, SURFACE AREA PORE, AND THERMAL PROPERTIES OF ZEOLITES FROM BAYAH, TASIKMALAYA, AND LAMPUNG. Characterization of chemical composition, surface area, pore radius, adsorption, and thermal properties of zeolites from Bayah, Tasikmalaya, and Lampung have been performed. The purpose of the characterization is to understand the characteristics of the three zeolites since different types of zeolite will yield different chemical composition, surface area, pore radius, and adsorption. The analysis shows that zeolites from Bayah, Tasikmalaya, and Lampung consist of chemical elements Al, Si, P, K, Ca, Ti, Fe, and S. The analysis of the surface area indicates that zeolite from Lampung has surface area of 10.0477 m², pore radius of 16.0653 Å, and adsorption of 24.500 ml/g, which are greater than those of zeolite from Tasikmalaya with surface area of 6.3319 m², pore radius of 16.2350 Å, adsorption of 13.2500 ml/g, zeolite from Bayah with surface area of 8.3528 m², pore radius of 16.2350 Å, and adsorption of 13.250 ml/g. From of the thermal properties characterization it is shown the three zeolites experienced weight reduction from 5.93% to 8.33%, which results in the formation of new phases as indicated by endothermic reactions from 150 °C to 600 °C and from 850 °C to 1000 °C. The three zeolites experienced a decrease in heat capacity up to temperature of 199.96 °C, whereas at temperatures above 216.66 °C the zeolites experienced an increase in heat capacity up to 437.78 °C. The results of the characterization indicate that different types of zeolite do not yield significant difference in chemical composition and thermal characteristics as proven with F test, however different surface area, pore radius, and adsorption characteristics are observed. The characterization results are expected to be the first step in determining the characteristics of the three zeolites that are to be used for cesium ion exchange in the incoming research.

FREE TERMS: zeolite, chemical coomposition, surface area, pore radius, thermal characteristichs