PENUMBUHAN LAPIS LINDUNG NITRIDA PADA PERMUKAAN BAHAN STRUKTUR REAKTOR PADUAN FeCrNi

Ari Handayani, Sulistioso GS, Nurdin Effendi, Sumarmo Sumarmo, Suprapto Suprapto

DOI: http://dx.doi.org/10.17146/urania.2013.19.2.1769

Sari


ABSTRAK
PENUMBUHAN LAPIS LINDUNG NITRIDA PADA PERMUKAAN BAHAN STRUKTUR
REAKTOR PADUAN FeCrNi. Percobaan penumbuhan lapis lindung nitrida pada paduan FeCrNi
telah dilakukan dengan metode plasma nitridasi untuk meningkatkan nilai kekerasannya,
ketahanan korosi dalam lingkungan air pendingin. Percobaan dilakukan pada temperatur 400 °C
dengan variasi nitridasi waktu pada 2 jam, 3 jam dan 4 jam. Karakterisasi meliputi pola difraksi
menggunakan X-Ray Diffractometer (XRD), struktumikro menggunakan Scanning Electron
Microscope - Energy Dispersive Spectrometer (SEM-EDS), kekerasan menggunakan Vicker’s
Hardness Tester dan uji korosi menggunakan Potensiostat Galvanostat Hasil nitridasi dari
pengamatan strukturmikro menunjukkan terbentuknya lapisan tipis pada permukaan paduan
FeCrNi. Pola difraksi sinar X menunjukkan bahwa terbentuk senyawa Fe2N dan Fe4N pada
permukaan paduan FeCrNi. Hasil uji kekerasan menunjukkan adanya peningkatan nilai
kekerasannya setelah proses nitridasi dari 235,97 VHN menjadi 271,76 VHN dan hasil uji korosi
dalam larutan air pendingin pH 6,3 juga ada peningkatan yaitu dari 0,0357 mpy menjadi
0,0032 mpy.
Kata kunci: plasma nitridasi, paduan FeCrNi, bahan struktur reaktor.

ABSTRACT
PROTECTING SURFACE LAYER OF NITRIDE ON STRUCTURE REACTOR MATERIAL OF
FeCrNi ALLOY. Experiment on the growth of protecting nitride layer on non standard FeCrNi
alloy has been done with plasma nitriding method. The research aims to increase the value of its
hardness and corrosión resistance in cooling wáter environment. The plasma nitriding was
carried out at a temperature of 400 °C with a variation of nitriding time, i.e. 2, 3 and 4 hours.
Included in the characterization are X-ray diffraction pattern using X-Ray Diffractometer (XRD),
microstructure - elemental composition examination using SEM-EDS, hardness (Vicker’s
hardness), and corrosion test (Potensiostat Galvanostat). The results show that the thin layer of
Fe-N coating was formed on the surface of FeCrNi alloy. The X-ray diffraction pattern shows that
the compounds of the thin layer are Fe2N and Fe4N. Characterization of hardness indicates that
the hardness increases after the nitriding process from 235.97 VHN to 271.76 VHN, while the corrosion test in cooling wáter with a solution pH of 6.3 shows enhanced corrosión resistance of
FeCrNi when compared to the condition before the formation of the thin layer, i.e. from
0.0357 mpy to 0.0032 mpy.
Keywords: plasma nitridation, FeCrNi, material structure.