APLIKASI SPEKTROMETER EMISI PADA ANALISIS UNSUR-UNSUR BAHAN PADUAN ALUMINIUM AlMgSi-1

Sari

ABSTRAK

APLIKASI SPEKTROMETER EMISI PADA ANALISIS UNSUR-UNSUR BAHAN PADUAN ALUMINIUM AlMgSi-1. Analisis unsur-unsur kelumit (Si, Mn, Cu, Ti, Ni, Cr, Mg) dalam paduan aluminium AlMgSi-1 telah dilakukan dengan metode uji ASTM menggunakan alat spektrometer emisi. Analisis dilakukan setelah alat uji dikalibrasi dengan mengukur beberapa bahan standar aluminium dengan berbagai konsentrasi. Hasil kalibrasi berupa kurva kalibrasi, yang menggambarkan hubungan antara konsentrasi dan intensitas pengukuran. Dari hasil evaluasi terhadap kurva kalibrasi dengan menggunakan metode kuadrat terkecil (least square) didapatkan daerah pengukuran linier, persamaan linier dan koefisien regresi serta limit deteksi. Dari hasil tersebut diperoleh ketepatan cukup baik antara persamaan linier dengan data pengukuran yang ditunjukkan dari nilai koefisien regresi pengukuran (0,997 hingga 0,999) yang berada dalam daerah yang dipersyaratkan (0,96). Ketepatan dan ketelitian pengukuran diperoleh dari pengukuran bahan standar sebanyak 7 kali pengulangan yang memiliki konsentrasi dalam daerah linieritas. Uji kuadrat chi (chi square) dengan tingkat kepercayaan 95% menunjukkan bahwa presisi pengukuran masih dalam batas yang diterima, sedangkan akurasi pengukuran dihitung dengan membandingkan nilai hasil pengukuran dengan nilai acuan dan diperoleh berkisar antara 95% hingga 99,97%. Dengan menggunakan alat yang telah terkalibrasi tersebut di atas maka dilakukan analisis terhadap bahan AlMgSi-1. Secara kualitatif sebagian besar unsur yang terkandung dalam bahan AlMgSi-1 dapat terdeteksi. Diantara unsur-unsur Si, Mn, Cu, Ti, Ni, Cr dan Mg yang ditentukan secara kuantitatif, hanya unsur Cr yang konsentrasinya diperoleh secara lebih akurat.

KATA KUNCI: Analisis unsur, Spektrometri emisi, Paduan aluminium

ABSTRACT

APPLICATION OF EMISSION SPECTROMETER FOR ANALYSES OF ALLOYING ELEMENTS OF ALUMINIUM ALLOY AlMgSi-1. Analyses of trace elements (Si, Mn, Cu, Ti, Ni, Cr, Mg) in aluminium alloy AlMgSi-1 were carried out using Emission Spectrometer (OES) in accordance with ASTM testing methods. The analyses were performed after the instrument was calibrated by measuring a number of aluminium standards at various concentrations. The calibration curves obtained depicted the correlation between standard concentration versus intensity. From the evaluation of calibration curves using the least square method, data on linear working range, linear equation, regression coefficient and detection limit were obtained. The results showed satisfactory precision between the linear equation and the measurement data, indicated by the fact that the regression coefficient values (0.997 up to 0.999) were within the required working area (0.96). The measurement precision and accuracy were acquired from the measurement of standard materials, repeated 7 times, in which the concentrations were found to be in the linearity range. Chi square test at 95% confidence level showed that measurement precision was within the acceptable limit, whereas themeasurement accuracy determined by comparing measurement results with referenced values was about 95% - 99.97%. Using the calibrated instrument, analyses on AlMgSi-1 alloyed samples were conducted. Most elements could be detected qualitatively. Among the quantitatively measured elements Si, Mn, Ti, Ni, Cr and Mg, only the concentration of Cr element could be determined accurately.

FREE TERMS: Element analyses, Emission spectrometer, Aluminium alloys accurately.